In Situ Measurements of Bridged Crack Interfaces in the Scanning Electron Microscope

Rödel, Jürgen ; Kelly, James F. ; Lawn, Brian R. (1990)
In Situ Measurements of Bridged Crack Interfaces in the Scanning Electron Microscope.
In: Journal of the American Ceramic Society, 73 (11)
doi: 10.1111/j.1151-2916.1990.tb06454.x
Artikel, Bibliographie

Kurzbeschreibung (Abstract)

A device for in situ SEM examination of crack propagation during loading of compact tension specimens is described, with a specific demonstration on an alumina ceramic. The device facilitates direct qualitative observations of the inception and subsequent frictional pullout of grain-localized bridges at the crack interface. Quantitative data on the bridging mechanism are obtained from measurements of the crack-opening displacements behind the crack tip. The crack profile is found to be closer to linear than parabolic at the bridged interface. Deconvolution of these crack-opening data allow for an evaluation of the closure tractions operative at the crack walls within the bridging zone, and thence the R-curve.

Typ des Eintrags: Artikel
Erschienen: 1990
Autor(en): Rödel, Jürgen ; Kelly, James F. ; Lawn, Brian R.
Art des Eintrags: Bibliographie
Titel: In Situ Measurements of Bridged Crack Interfaces in the Scanning Electron Microscope
Sprache: Englisch
Publikationsjahr: November 1990
Titel der Zeitschrift, Zeitung oder Schriftenreihe: Journal of the American Ceramic Society
Jahrgang/Volume einer Zeitschrift: 73
(Heft-)Nummer: 11
DOI: 10.1111/j.1151-2916.1990.tb06454.x
Kurzbeschreibung (Abstract):

A device for in situ SEM examination of crack propagation during loading of compact tension specimens is described, with a specific demonstration on an alumina ceramic. The device facilitates direct qualitative observations of the inception and subsequent frictional pullout of grain-localized bridges at the crack interface. Quantitative data on the bridging mechanism are obtained from measurements of the crack-opening displacements behind the crack tip. The crack profile is found to be closer to linear than parabolic at the bridged interface. Deconvolution of these crack-opening data allow for an evaluation of the closure tractions operative at the crack walls within the bridging zone, and thence the R-curve.

Freie Schlagworte: scanning electron microscopy; cracks; bridging; pullout; toughness
Fachbereich(e)/-gebiet(e): 11 Fachbereich Material- und Geowissenschaften > Materialwissenschaft > Fachgebiet Nichtmetallisch-Anorganische Werkstoffe
11 Fachbereich Material- und Geowissenschaften > Materialwissenschaft
11 Fachbereich Material- und Geowissenschaften
Hinterlegungsdatum: 13 Jun 2012 12:20
Letzte Änderung: 05 Mär 2013 10:01
PPN:
Export:
Suche nach Titel in: TUfind oder in Google
Frage zum Eintrag Frage zum Eintrag

Optionen (nur für Redakteure)
Redaktionelle Details anzeigen Redaktionelle Details anzeigen