In Situ XRD of Highly Charged and Discharged Li<em>x</em>Ni0.8Co0.2O2 (<em>x</em> close to 0)

Nikolowski, Kristian M. ; Bramnik, Natalia N. ; Baehtz, Christian ; Ehrenberg, Helmut ; Fuess, Hartmut (2005)
In Situ XRD of Highly Charged and Discharged Li<em>x</em>Ni0.8Co0.2O2 (<em>x</em> close to 0).
In: Rechargeable Lithium and Lithium-Ion Batteries Editor(s): J. Weidner, 1 (26)
Artikel, Bibliographie

Kurzbeschreibung (Abstract)

Lithium has been electrochemically extracted and inserted fromLixNi0.8Co0.2O2 (0{less than or equal to}xLi{less than or equal to}1) using a dedicated electrochemicalcell. The behavior of this cathode material for lithiumbatteries was studied by in situ-X-ray diffraction usingsynchrotron radiation and analyzed by Rietveld refinement.Besides the accurate determination of the lattice parametersduring cycling, an anisotropic broadening of specificreflections, most pronounced around xLi=0.1, is observed andattributed to reversible microstructural changes at this highdegree of lithium extraction.

Typ des Eintrags: Artikel
Erschienen: 2005
Autor(en): Nikolowski, Kristian M. ; Bramnik, Natalia N. ; Baehtz, Christian ; Ehrenberg, Helmut ; Fuess, Hartmut
Art des Eintrags: Bibliographie
Titel: In Situ XRD of Highly Charged and Discharged Li<em>x</em>Ni0.8Co0.2O2 (<em>x</em> close to 0)
Sprache: Englisch
Publikationsjahr: Oktober 2005
Verlag: ECS Transactions
Titel der Zeitschrift, Zeitung oder Schriftenreihe: Rechargeable Lithium and Lithium-Ion Batteries Editor(s): J. Weidner
Jahrgang/Volume einer Zeitschrift: 1
(Heft-)Nummer: 26
URL / URN: http://www.ecsdl.org/getabs/servlet/GetabsServlet?prog=norma...
Kurzbeschreibung (Abstract):

Lithium has been electrochemically extracted and inserted fromLixNi0.8Co0.2O2 (0{less than or equal to}xLi{less than or equal to}1) using a dedicated electrochemicalcell. The behavior of this cathode material for lithiumbatteries was studied by in situ-X-ray diffraction usingsynchrotron radiation and analyzed by Rietveld refinement.Besides the accurate determination of the lattice parametersduring cycling, an anisotropic broadening of specificreflections, most pronounced around xLi=0.1, is observed andattributed to reversible microstructural changes at this highdegree of lithium extraction.

Zusätzliche Informationen:

SFB 595 B4

Fachbereich(e)/-gebiet(e): DFG-Sonderforschungsbereiche (inkl. Transregio) > Sonderforschungsbereiche > SFB 595: Elektrische Ermüdung > B - Charakterisierung > Teilprojekt B4: In situ Untersuchungen der Degradation von Interkalationsbatterien und deren Modellierung
DFG-Sonderforschungsbereiche (inkl. Transregio) > Sonderforschungsbereiche > SFB 595: Elektrische Ermüdung > B - Charakterisierung
DFG-Sonderforschungsbereiche (inkl. Transregio) > Sonderforschungsbereiche > SFB 595: Elektrische Ermüdung
Zentrale Einrichtungen
DFG-Sonderforschungsbereiche (inkl. Transregio) > Sonderforschungsbereiche
DFG-Sonderforschungsbereiche (inkl. Transregio)
Hinterlegungsdatum: 27 Sep 2011 09:18
Letzte Änderung: 05 Mär 2013 09:54
PPN:
Export:
Suche nach Titel in: TUfind oder in Google
Frage zum Eintrag Frage zum Eintrag

Optionen (nur für Redakteure)
Redaktionelle Details anzeigen Redaktionelle Details anzeigen