Vacancy-like defects in doped Pb(Zr60Ti40)O-3 observed by positron lifetime and coincident Doppler spectroscopy

Puff, Werner ; Kungl, Hans ; Hoffmann, Michael J. ; Gottschalk, Sebastian ; Balogh, Adam G. (2004)
Vacancy-like defects in doped Pb(Zr60Ti40)O-3 observed by positron lifetime and coincident Doppler spectroscopy.
In: POSITRON ANNIHILATION, ICPA-13, PROCEEDINGS, 445 (6)
Artikel, Bibliographie

Kurzbeschreibung (Abstract)

Ferroelectric Pb(Zr60Ti40)O-3 ceramics sintered for 6 hours at 1050 degreesC in air and doped with La or Nb in the range 0.5 to 6 mol% have been investigated by positron lifetime spectroscopy and two-dimensional coincident Doppler measurements. The undoped samples show two lifetime components with a defect lifetime of about 250 ps. After doping this defect lifetime increases to about 295 ps. The influence of the doping on the Doppler spectra is extremely small. Additional XRD pattern show a significant correlation between doping and lattice structure.

Typ des Eintrags: Artikel
Erschienen: 2004
Autor(en): Puff, Werner ; Kungl, Hans ; Hoffmann, Michael J. ; Gottschalk, Sebastian ; Balogh, Adam G.
Art des Eintrags: Bibliographie
Titel: Vacancy-like defects in doped Pb(Zr60Ti40)O-3 observed by positron lifetime and coincident Doppler spectroscopy
Sprache: Englisch
Publikationsjahr: 10 August 2004
Verlag: MATERIALS SCIENCE FORUM
Titel der Zeitschrift, Zeitung oder Schriftenreihe: POSITRON ANNIHILATION, ICPA-13, PROCEEDINGS
Jahrgang/Volume einer Zeitschrift: 445
(Heft-)Nummer: 6
URL / URN: http://www.scientific.net/0-87849-936-9/171/
Kurzbeschreibung (Abstract):

Ferroelectric Pb(Zr60Ti40)O-3 ceramics sintered for 6 hours at 1050 degreesC in air and doped with La or Nb in the range 0.5 to 6 mol% have been investigated by positron lifetime spectroscopy and two-dimensional coincident Doppler measurements. The undoped samples show two lifetime components with a defect lifetime of about 250 ps. After doping this defect lifetime increases to about 295 ps. The influence of the doping on the Doppler spectra is extremely small. Additional XRD pattern show a significant correlation between doping and lattice structure.

Freie Schlagworte: coincident Doppler spectroscopy; defects; ferroelectrics; positron lifetime; PZT; XRD; ANNIHILATION; CERAMICS
Zusätzliche Informationen:

SFB 595 Cooperation A2, B2; ISBN: 0-87849-936-9 IDS Number: BY55H

Fachbereich(e)/-gebiet(e): DFG-Sonderforschungsbereiche (inkl. Transregio)
DFG-Sonderforschungsbereiche (inkl. Transregio) > Sonderforschungsbereiche
Zentrale Einrichtungen
DFG-Sonderforschungsbereiche (inkl. Transregio) > Sonderforschungsbereiche > SFB 595: Elektrische Ermüdung
DFG-Sonderforschungsbereiche (inkl. Transregio) > Sonderforschungsbereiche > SFB 595: Elektrische Ermüdung > A - Synthese
DFG-Sonderforschungsbereiche (inkl. Transregio) > Sonderforschungsbereiche > SFB 595: Elektrische Ermüdung > A - Synthese > Teilprojekt A2: Herstellung und Charakterisierung von PZT-Keramiken mit definierter Defektchemie
DFG-Sonderforschungsbereiche (inkl. Transregio) > Sonderforschungsbereiche > SFB 595: Elektrische Ermüdung > B - Charakterisierung
DFG-Sonderforschungsbereiche (inkl. Transregio) > Sonderforschungsbereiche > SFB 595: Elektrische Ermüdung > B - Charakterisierung > Teilprojekt B2: Untersuchung der Defektstruktur und Diffusion in ferroelektrischen Materialien
Hinterlegungsdatum: 10 Aug 2011 11:15
Letzte Änderung: 26 Jan 2024 10:40
PPN:
Export:
Suche nach Titel in: TUfind oder in Google
Frage zum Eintrag Frage zum Eintrag

Optionen (nur für Redakteure)
Redaktionelle Details anzeigen Redaktionelle Details anzeigen