Xu, J. ; Bellas, V. ; Jungnickel, B.-J. ; Stühn, B. ; Rehahn, M. (2011)
Equilibrium Melting Temperature of Poly(ferrocenyl dimethylsilane) in Homopolymers and Lamellar Diblock Copolymers with Polystyrene.
In: MACROMOLECULAR CHEMISTRY AND PHYSICS, 211 (11)
doi: 10.1002/macp.200900718
Artikel, Bibliographie
Kurzbeschreibung (Abstract)
The equilibrium melting temperature, T-m,T-o, of poly(ferrocenyl dimethylsilane) (PFDMS) is re-investigated using two PFDMS homopolymers and a PS-b-PFDMS copolymer (PS: polystyrene). The melting temperatures of samples crystallized at different crystallization temperatures, T-c, were found to depend in a nonlinear fashion on T-c. Consequently, the Hoffmann Weeks approach fails in determining T-m,T-o. The more reliable Gibbs Thomson approach results in a T-m,T-o = (215 +/- 11) degrees C for the PFDMS homopolymers, and a T-m,T-o = (179 +/- 5) degrees C for the PFDMS microphases in the lamellar PS-b-PFDMS diblock copolymer.
| Typ des Eintrags: | Artikel |
|---|---|
| Erschienen: | 2011 |
| Autor(en): | Xu, J. ; Bellas, V. ; Jungnickel, B.-J. ; Stühn, B. ; Rehahn, M. |
| Art des Eintrags: | Bibliographie |
| Titel: | Equilibrium Melting Temperature of Poly(ferrocenyl dimethylsilane) in Homopolymers and Lamellar Diblock Copolymers with Polystyrene |
| Sprache: | Englisch |
| Publikationsjahr: | 11 Mai 2011 |
| Titel der Zeitschrift, Zeitung oder Schriftenreihe: | MACROMOLECULAR CHEMISTRY AND PHYSICS |
| Jahrgang/Volume einer Zeitschrift: | 211 |
| (Heft-)Nummer: | 11 |
| DOI: | 10.1002/macp.200900718 |
| Kurzbeschreibung (Abstract): | The equilibrium melting temperature, T-m,T-o, of poly(ferrocenyl dimethylsilane) (PFDMS) is re-investigated using two PFDMS homopolymers and a PS-b-PFDMS copolymer (PS: polystyrene). The melting temperatures of samples crystallized at different crystallization temperatures, T-c, were found to depend in a nonlinear fashion on T-c. Consequently, the Hoffmann Weeks approach fails in determining T-m,T-o. The more reliable Gibbs Thomson approach results in a T-m,T-o = (215 +/- 11) degrees C for the PFDMS homopolymers, and a T-m,T-o = (179 +/- 5) degrees C for the PFDMS microphases in the lamellar PS-b-PFDMS diblock copolymer. |
| Fachbereich(e)/-gebiet(e): | 05 Fachbereich Physik > Institut für Festkörperphysik (2021 umbenannt in Institut für Physik Kondensierter Materie (IPKM)) > Experimentelle Physik kondensierter Materie 05 Fachbereich Physik > Institut für Festkörperphysik (2021 umbenannt in Institut für Physik Kondensierter Materie (IPKM)) 05 Fachbereich Physik |
| Hinterlegungsdatum: | 17 Mai 2011 04:54 |
| Letzte Änderung: | 05 Mär 2013 09:47 |
| PPN: | |
| Export: | |
| Suche nach Titel in: | TUfind oder in Google |
 |
Frage zum Eintrag |
Optionen (nur für Redakteure)
 |
Redaktionelle Details anzeigen |
Drucken
Impressum