Klitsch, Johannes ; Pfaendner, Rudolf ; Fasel, Claudia ; Schönberger, Frank (2022)
Mode of Action of Zn-DOPOx and Melamine Polyphosphate as Flame Retardants in Glass Fiber-Reinforced Polyamide 66.
In: Polymers, 14 (18)
doi: 10.3390/polym14183709
Artikel, Bibliographie
Dies ist die neueste Version dieses Eintrags.
Kurzbeschreibung (Abstract)
In this study, the flame retardant effect of the Zn salt of 10-hydroxy-9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (Zn-DOPOx), melamine polyphosphate (MPP) and their mixture was investigated towards the mode of action in glass fiber-reinforced polyamide 66 (PA 66 GF). The flammability was evaluated using UL 94 V and cone calorimetry. Influence on char formation was analyzed by SEM. Thermal decomposition of Zn-DOPOx and MPP was studied by TGA and ATR-FTIR. The release of gaseous PA 66 decomposition products was investigated using TGA-DTA-FTIR. Combining Zn-DOPOx and MPP leads to an improvement in flame retardancy, most pronounced for equal parts of weight. Mode of action changes significantly for Zn-DOPOx:MPP (1:1) compared to the sole components and a strong interaction between Zn-DOPOx and MPP is revealed, resulting in a more open char structure. Fuel dilution as well as less exothermic decomposition are essential for the mode of action of the combination. Through low HRR values and high CO/CO2 ratio during cone calorimetry measurements, a significant increase in gas phase activity was proven. Therefore, it is concluded that Zn-DOPOx:MPP (1:1) leads to a significant increase in flame retardancy through a combination of mode of actions in the gas and condensed phase resulting from the change in thermal stability.
| Typ des Eintrags: | Artikel |
|---|---|
| Erschienen: | 2022 |
| Autor(en): | Klitsch, Johannes ; Pfaendner, Rudolf ; Fasel, Claudia ; Schönberger, Frank |
| Art des Eintrags: | Bibliographie |
| Titel: | Mode of Action of Zn-DOPOx and Melamine Polyphosphate as Flame Retardants in Glass Fiber-Reinforced Polyamide 66 |
| Sprache: | Englisch |
| Publikationsjahr: | 6 September 2022 |
| Verlag: | MDPI |
| Titel der Zeitschrift, Zeitung oder Schriftenreihe: | Polymers |
| Jahrgang/Volume einer Zeitschrift: | 14 |
| (Heft-)Nummer: | 18 |
| DOI: | 10.3390/polym14183709 |
| Zugehörige Links: | |
| Kurzbeschreibung (Abstract): | In this study, the flame retardant effect of the Zn salt of 10-hydroxy-9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (Zn-DOPOx), melamine polyphosphate (MPP) and their mixture was investigated towards the mode of action in glass fiber-reinforced polyamide 66 (PA 66 GF). The flammability was evaluated using UL 94 V and cone calorimetry. Influence on char formation was analyzed by SEM. Thermal decomposition of Zn-DOPOx and MPP was studied by TGA and ATR-FTIR. The release of gaseous PA 66 decomposition products was investigated using TGA-DTA-FTIR. Combining Zn-DOPOx and MPP leads to an improvement in flame retardancy, most pronounced for equal parts of weight. Mode of action changes significantly for Zn-DOPOx:MPP (1:1) compared to the sole components and a strong interaction between Zn-DOPOx and MPP is revealed, resulting in a more open char structure. Fuel dilution as well as less exothermic decomposition are essential for the mode of action of the combination. Through low HRR values and high CO/CO2 ratio during cone calorimetry measurements, a significant increase in gas phase activity was proven. Therefore, it is concluded that Zn-DOPOx:MPP (1:1) leads to a significant increase in flame retardancy through a combination of mode of actions in the gas and condensed phase resulting from the change in thermal stability. |
| Freie Schlagworte: | Flame retardant, PA 66, phosphorus-containing flame retardant, metal phosphorous salt, halogen-free Epoxy-Resin, Combustion Behavior, Fire, Pyrolysis, Combination, Compossites, Inhibition, Phosphorus, Mechanisms, Nitrogen |
| Zusätzliche Informationen: | Paper No. 3709 |
| Fachbereich(e)/-gebiet(e): | 11 Fachbereich Material- und Geowissenschaften 11 Fachbereich Material- und Geowissenschaften > Materialwissenschaft 11 Fachbereich Material- und Geowissenschaften > Materialwissenschaft > Fachgebiet Disperse Feststoffe |
| Hinterlegungsdatum: | 28 Okt 2022 06:11 |
| Letzte Änderung: | 03 Jul 2024 02:58 |
| PPN: | |
| Export: | |
| Suche nach Titel in: | TUfind oder in Google |
Verfügbare Versionen dieses Eintrags
-
Mode of Action of Zn-DOPOx and Melamine Polyphosphate as Flame Retardants in Glass Fiber-Reinforced Polyamide 66. (deposited 10 Okt 2022 12:36)
- Mode of Action of Zn-DOPOx and Melamine Polyphosphate as Flame Retardants in Glass Fiber-Reinforced Polyamide 66. (deposited 28 Okt 2022 06:11) [Gegenwärtig angezeigt]
 |
Frage zum Eintrag |
Optionen (nur für Redakteure)
 |
Redaktionelle Details anzeigen |
Drucken
Impressum