Slabki, Mihail ; Kodumudi Venkataraman, Lalitha ; Rödel, Jürgen ; Koruza, Jurij (2022)
Origin of high-power drive stability in (Na 1/2 Bi 1/2 )TiO 3 -BaTiO 3 based piezoceramics.
In: Acta Materialia, 227
doi: 10.1016/j.actamat.2022.117703
Artikel, Bibliographie
Kurzbeschreibung (Abstract)
Hard-type ferroelectrics are indispensable and increasingly used for numerous high-power piezoelec- tric resonance applications, ranging from ultrasonic welding and cleaning, to voltage transformers and miniaturized ultrasonic motors in robotics. While the state-of-the-art lead-based ferroelectrics are hitting their operational limits, several new and environmentally-friendly lead-free alternative materials have emerged recently. Particularly compositions of the (Na 1/2 Bi 1/2 )TiO 3 family have demonstrated promising high-power properties and increased depolarization temperatures. However, the underlying mechanisms remain unclear and hamper further development of these materials. Here, we investigate the high-power electromechanical behavior of several (Na 1/2 Bi 1/2 )TiO 3 -based compositions and reveal that these exhibit an inherent intrinsic stability, which is retained at large vibration velocity and broad temperature range also after acceptor doping or composite formation. This results in excellent high-power figures of merit even at vibration velocities beyond 1 m/s, at which the lead-based compositions already fail. Moreover, the critical vibration velocity for fracture was found to be almost two-times higher for (Na 1/2 Bi 1/2 )TiO 3 - based materials, demonstrating their high dynamic fracture strength. The microscopic origin of this be- havior was identified using synchrotron radiation, revealing that the strain is dominated by lattice con- tributions, induced by the emerging mechanical stress. Due to the large coercive stress, the domain wall contributions are in the range of only 3–5% and, unlike in PZT, remain relatively constant also at higher vibration velocities. The high-power properties and stability are thus determined by the intrinsic loss instead of the usually-dominant extrinsic loss.
| Typ des Eintrags: | Artikel |
|---|---|
| Erschienen: | 2022 |
| Autor(en): | Slabki, Mihail ; Kodumudi Venkataraman, Lalitha ; Rödel, Jürgen ; Koruza, Jurij |
| Art des Eintrags: | Bibliographie |
| Titel: | Origin of high-power drive stability in (Na 1/2 Bi 1/2 )TiO 3 -BaTiO 3 based piezoceramics |
| Sprache: | Englisch |
| Publikationsjahr: | 9 Februar 2022 |
| Verlag: | Elsevier |
| Titel der Zeitschrift, Zeitung oder Schriftenreihe: | Acta Materialia |
| Jahrgang/Volume einer Zeitschrift: | 227 |
| DOI: | 10.1016/j.actamat.2022.117703 |
| Kurzbeschreibung (Abstract): | Hard-type ferroelectrics are indispensable and increasingly used for numerous high-power piezoelec- tric resonance applications, ranging from ultrasonic welding and cleaning, to voltage transformers and miniaturized ultrasonic motors in robotics. While the state-of-the-art lead-based ferroelectrics are hitting their operational limits, several new and environmentally-friendly lead-free alternative materials have emerged recently. Particularly compositions of the (Na 1/2 Bi 1/2 )TiO 3 family have demonstrated promising high-power properties and increased depolarization temperatures. However, the underlying mechanisms remain unclear and hamper further development of these materials. Here, we investigate the high-power electromechanical behavior of several (Na 1/2 Bi 1/2 )TiO 3 -based compositions and reveal that these exhibit an inherent intrinsic stability, which is retained at large vibration velocity and broad temperature range also after acceptor doping or composite formation. This results in excellent high-power figures of merit even at vibration velocities beyond 1 m/s, at which the lead-based compositions already fail. Moreover, the critical vibration velocity for fracture was found to be almost two-times higher for (Na 1/2 Bi 1/2 )TiO 3 - based materials, demonstrating their high dynamic fracture strength. The microscopic origin of this be- havior was identified using synchrotron radiation, revealing that the strain is dominated by lattice con- tributions, induced by the emerging mechanical stress. Due to the large coercive stress, the domain wall contributions are in the range of only 3–5% and, unlike in PZT, remain relatively constant also at higher vibration velocities. The high-power properties and stability are thus determined by the intrinsic loss instead of the usually-dominant extrinsic loss. |
| Freie Schlagworte: | Piezoceramics, High-power NBT, Lead-free |
| Zusätzliche Informationen: | Artikel-ID: 117703 |
| Fachbereich(e)/-gebiet(e): | 11 Fachbereich Material- und Geowissenschaften 11 Fachbereich Material- und Geowissenschaften > Materialwissenschaft 11 Fachbereich Material- und Geowissenschaften > Materialwissenschaft > Fachgebiet Nichtmetallisch-Anorganische Werkstoffe |
| Hinterlegungsdatum: | 10 Feb 2022 06:10 |
| Letzte Änderung: | 10 Feb 2022 06:10 |
| PPN: | |
| Export: | |
| Suche nach Titel in: | TUfind oder in Google |
 |
Frage zum Eintrag |
Optionen (nur für Redakteure)
 |
Redaktionelle Details anzeigen |
Drucken
Impressum