Amaya-Dueñas, Diana María ; Chen, Guoxing ; Weidenkaff, Anke ; Sata, Noriko ; Han, Feng ; Biswas, Indro ; Costa, Rémi ; Friedrich, Kaspar Andreas (2021)
A–site Deficient Chromite with In Situ Ni Exsolution as Fuel Electrode for Solid Oxide Cells (SOC).
In: Journal of Materials Chemistry A, 2021
doi: 10.1039/D0TA07090D
Artikel, Bibliographie
Kurzbeschreibung (Abstract)
A-site deficient lanthanum strontium chromite perovskite La0.65Sr0.3Cr0.85Ni0.15O3-δ (L65SCrN) decorated by in situ exsolution of Ni nanoparticles was synthesized and implemented as fuel electrode on a 5 cm x 5 cm electrolyte-supported cell (ESC) for solid oxide cells (SOC) with an active surface of 16 cm2. The stoichiometric formulation La0.70Sr0.3Cr0.85Ni0.15O3-δ (L70SCrN) was also prepared in order to evaluate the reducibility and behavior towards Ni exsolution with respect to L65SCrN. This comparison was assessed by means of X-ray diffraction (XRD) and thermogravimetric analysis (TGA) in reducing atmosphere. Metallic Ni was successfully detected by XRD on the A-site deficient formulation after TGA treatment. Surface analysis by means of X-ray photoemission spectroscopy (XPS) revealed a relative enrichment in Cr 3+. Ni exsolution was investigated on the L65SCrN formulation by annealing in reducing atmosphere at 500°C and 900°C for 3 hours. Ni nanoparticles size (from ~8 up to 100 nm) and morphology were characterized by means of scanning electron microscopy (SEM). Furthermore, L65SCrN was screen printed onto a 90 μm thick CGO20-3YSZ-CGO20 electrolyte on which the oxygen electrode La0.58Sr0.4Fe0.8Co0.2O3-δ (LSCF) was printed on the other side. With ideal contacting, the electrochemical cell performance with the L65SCrN fuel electrode demonstrated to be comparable to those with the state-of-the-art Ni-based cermets: the ASRDC_Total at -0.3 A•cm-2 was calculated to be 0.676 Ω•cm2 in co-electrolysis operation. Reversible operation (rSOC) at 860°C with H2O/H2 ratio of 1 could be shown and co-electrolysis operation (H2O/CO2=2) at -0.45A•cm-2 and 860°C with a voltage degradation of less than 3.5mV/1000 hours could be demonstrated during 950 hours. Even though L65SCrN showed promising results for SOC operation, further investigations of Ni exsolution in doped chromites by varying temperature, time and pO2 are proposed for detailed understanding and optimization of the Ni nanoparticle size.
| Typ des Eintrags: | Artikel |
|---|---|
| Erschienen: | 2021 |
| Autor(en): | Amaya-Dueñas, Diana María ; Chen, Guoxing ; Weidenkaff, Anke ; Sata, Noriko ; Han, Feng ; Biswas, Indro ; Costa, Rémi ; Friedrich, Kaspar Andreas |
| Art des Eintrags: | Bibliographie |
| Titel: | A–site Deficient Chromite with In Situ Ni Exsolution as Fuel Electrode for Solid Oxide Cells (SOC) |
| Sprache: | Englisch |
| Publikationsjahr: | 1 Februar 2021 |
| Verlag: | Royal Society of Chemistry |
| Titel der Zeitschrift, Zeitung oder Schriftenreihe: | Journal of Materials Chemistry A |
| Jahrgang/Volume einer Zeitschrift: | 2021 |
| DOI: | 10.1039/D0TA07090D |
| Kurzbeschreibung (Abstract): | A-site deficient lanthanum strontium chromite perovskite La0.65Sr0.3Cr0.85Ni0.15O3-δ (L65SCrN) decorated by in situ exsolution of Ni nanoparticles was synthesized and implemented as fuel electrode on a 5 cm x 5 cm electrolyte-supported cell (ESC) for solid oxide cells (SOC) with an active surface of 16 cm2. The stoichiometric formulation La0.70Sr0.3Cr0.85Ni0.15O3-δ (L70SCrN) was also prepared in order to evaluate the reducibility and behavior towards Ni exsolution with respect to L65SCrN. This comparison was assessed by means of X-ray diffraction (XRD) and thermogravimetric analysis (TGA) in reducing atmosphere. Metallic Ni was successfully detected by XRD on the A-site deficient formulation after TGA treatment. Surface analysis by means of X-ray photoemission spectroscopy (XPS) revealed a relative enrichment in Cr 3+. Ni exsolution was investigated on the L65SCrN formulation by annealing in reducing atmosphere at 500°C and 900°C for 3 hours. Ni nanoparticles size (from ~8 up to 100 nm) and morphology were characterized by means of scanning electron microscopy (SEM). Furthermore, L65SCrN was screen printed onto a 90 μm thick CGO20-3YSZ-CGO20 electrolyte on which the oxygen electrode La0.58Sr0.4Fe0.8Co0.2O3-δ (LSCF) was printed on the other side. With ideal contacting, the electrochemical cell performance with the L65SCrN fuel electrode demonstrated to be comparable to those with the state-of-the-art Ni-based cermets: the ASRDC_Total at -0.3 A•cm-2 was calculated to be 0.676 Ω•cm2 in co-electrolysis operation. Reversible operation (rSOC) at 860°C with H2O/H2 ratio of 1 could be shown and co-electrolysis operation (H2O/CO2=2) at -0.45A•cm-2 and 860°C with a voltage degradation of less than 3.5mV/1000 hours could be demonstrated during 950 hours. Even though L65SCrN showed promising results for SOC operation, further investigations of Ni exsolution in doped chromites by varying temperature, time and pO2 are proposed for detailed understanding and optimization of the Ni nanoparticle size. |
| Fachbereich(e)/-gebiet(e): | 11 Fachbereich Material- und Geowissenschaften 11 Fachbereich Material- und Geowissenschaften > Materialwissenschaft 11 Fachbereich Material- und Geowissenschaften > Materialwissenschaft > Werkstofftechnik und Ressourcenmanagement |
| Hinterlegungsdatum: | 03 Feb 2021 10:14 |
| Letzte Änderung: | 03 Feb 2021 13:16 |
| PPN: | |
| Export: | |
| Suche nach Titel in: | TUfind oder in Google |
 |
Frage zum Eintrag |
Optionen (nur für Redakteure)
 |
Redaktionelle Details anzeigen |
Drucken
Impressum