Groh, Claudia ; Kobayashi, Keisuke ; Shimizu, Hiroyuki ; Doshida, Yutaka ; Mizuno, Youichi ; Patterson, Eric A. ; Rödel, Jürgen (2016)
High-Temperature Multilayer Ceramic Capacitors Based on
100–x(94Bi1/2Na1/2TiO3–6BaTiO3)–xK0.5Na0.5NbO.
In: Journal of the American Ceramic Society, 99 (6)
doi: 10.1111/jace.14097
Article, Bibliographie
Abstract
The potential high-temperature dielectric materials 100 – x (94Bi1/2Na1/2TiO3–6BaTiO3)–xK0.5Na0.5NbO3 with x = 12, 18, and 24 were processed as bulk samples in order to examine the reduction of sintering temperature by means of CuO as sintering aid. Due to the successful reduction of sintering temperature, low cost Ag:Pd could be used as a co-fired electrode material for multilayer ceramic capacitors (MLCCs). Fabrication of 8 lm thick, dense MLCCs with self-contained, nonreactive electrodes is reported for a wide range of compositions of Bi1/2Na1/2TiO3–BaTiO3–K0.5Na0.5NbO3. Among the manufactured MLCCs, those with compositions x = 24 showed the most promising dielectric properties for applications where high operating temperatures are needed. The temperature-dependence of permittivity was quite low, revealing a change of less than +-10% compared to its 150°C-value in the range of 40°C–225°C. For samples sintered at 1000°C, an RC constant of about 300 s was obtained at 150°C. Furthermore, these x = 24MLCCs exhibited the finest microstructures among the compositions examined; making it a suitable candidate for further miniaturization of layer thickness as required for state-of-the art devices.
| Item Type: | Article |
|---|---|
| Erschienen: | 2016 |
| Creators: | Groh, Claudia ; Kobayashi, Keisuke ; Shimizu, Hiroyuki ; Doshida, Yutaka ; Mizuno, Youichi ; Patterson, Eric A. ; Rödel, Jürgen |
| Type of entry: | Bibliographie |
| Title: | High-Temperature Multilayer Ceramic Capacitors Based on 100–x(94Bi1/2Na1/2TiO3–6BaTiO3)–xK0.5Na0.5NbO |
| Language: | English |
| Date: | 6 June 2016 |
| Publisher: | The American Ceramic Society |
| Journal or Publication Title: | Journal of the American Ceramic Society |
| Volume of the journal: | 99 |
| Issue Number: | 6 |
| DOI: | 10.1111/jace.14097 |
| Abstract: | The potential high-temperature dielectric materials 100 – x (94Bi1/2Na1/2TiO3–6BaTiO3)–xK0.5Na0.5NbO3 with x = 12, 18, and 24 were processed as bulk samples in order to examine the reduction of sintering temperature by means of CuO as sintering aid. Due to the successful reduction of sintering temperature, low cost Ag:Pd could be used as a co-fired electrode material for multilayer ceramic capacitors (MLCCs). Fabrication of 8 lm thick, dense MLCCs with self-contained, nonreactive electrodes is reported for a wide range of compositions of Bi1/2Na1/2TiO3–BaTiO3–K0.5Na0.5NbO3. Among the manufactured MLCCs, those with compositions x = 24 showed the most promising dielectric properties for applications where high operating temperatures are needed. The temperature-dependence of permittivity was quite low, revealing a change of less than +-10% compared to its 150°C-value in the range of 40°C–225°C. For samples sintered at 1000°C, an RC constant of about 300 s was obtained at 150°C. Furthermore, these x = 24MLCCs exhibited the finest microstructures among the compositions examined; making it a suitable candidate for further miniaturization of layer thickness as required for state-of-the art devices. |
| Divisions: | 11 Department of Materials and Earth Sciences 11 Department of Materials and Earth Sciences > Material Science 11 Department of Materials and Earth Sciences > Material Science > Nonmetallic-Inorganic Materials |
| Date Deposited: | 07 Jun 2016 05:34 |
| Last Modified: | 07 Jun 2016 05:34 |
| PPN: | |
| Export: | |
| Suche nach Titel in: | TUfind oder in Google |
 |
Send an inquiry |
Options (only for editors)
 |
Show editorial Details |
Drucken
Impressum