Li, Wenjie and Gurlo, Aleksander and Riedel, Ralf and Ionescu, Emanuel (2015):
Perovskite-type Solid Solution SrMo1-xWx(O,N)3xynitrides: Synthesis, Structure, and Magnetic Properties.
In: Zeitschrift für anorganische und allgemeine Chemie, 641 (8-9), pp. 1533-1539. WILEY-VCH Verlag GmbH & Co. KGaA, ISSN 00442313,
[Article]
Abstract
Phase-pure scheelite-type solid solution SrMo1–xWxO4 oxides (x = 0.05, 0.15, 0.25, 0.4, 0.5, 0.6, 0.75, 0.85, 0.95) were synthesized by solvothermal methods and subsequently thermally treated in ammonia atmosphere at temperatures between 700 and 900 °C. As revealed by X-ray diffraction (XRD) and neutron diffraction as well as elemental analysis data, SrMo1–xWxO4 convert into their corresponding solid solution perovskite-type oxynitrides SrMo1–xWx(O, N)3 only for x ≤ 0.25 and x ≥ 0.6; whereas for 0.25 ≤ x ≤ 0.6 the formation of Sr3WO6 with double perovskite structure and of other binary oxides and nitrides was observed. The solid solution oxynitrides were investigated concerning their magnetic properties. Thus, the magnetic susceptibility of the SrMo1–xWx(O, N)3 oxynitride samples was measured by Superconducting Quantum Interference Device (SQUID). The influence of different parameters (such as phase composition, ratio between Mo and W or nitrogen content) on the magnetic behavior in the solid solution oxynitrides is briefly discussed.
Item Type: | Article |
---|---|
Erschienen: | 2015 |
Creators: | Li, Wenjie and Gurlo, Aleksander and Riedel, Ralf and Ionescu, Emanuel |
Title: | Perovskite-type Solid Solution SrMo1-xWx(O,N)3xynitrides: Synthesis, Structure, and Magnetic Properties |
Language: | English |
Abstract: | Phase-pure scheelite-type solid solution SrMo1–xWxO4 oxides (x = 0.05, 0.15, 0.25, 0.4, 0.5, 0.6, 0.75, 0.85, 0.95) were synthesized by solvothermal methods and subsequently thermally treated in ammonia atmosphere at temperatures between 700 and 900 °C. As revealed by X-ray diffraction (XRD) and neutron diffraction as well as elemental analysis data, SrMo1–xWxO4 convert into their corresponding solid solution perovskite-type oxynitrides SrMo1–xWx(O, N)3 only for x ≤ 0.25 and x ≥ 0.6; whereas for 0.25 ≤ x ≤ 0.6 the formation of Sr3WO6 with double perovskite structure and of other binary oxides and nitrides was observed. The solid solution oxynitrides were investigated concerning their magnetic properties. Thus, the magnetic susceptibility of the SrMo1–xWx(O, N)3 oxynitride samples was measured by Superconducting Quantum Interference Device (SQUID). The influence of different parameters (such as phase composition, ratio between Mo and W or nitrogen content) on the magnetic behavior in the solid solution oxynitrides is briefly discussed. |
Journal or Publication Title: | Zeitschrift für anorganische und allgemeine Chemie |
Journal volume: | 641 |
Number: | 8-9 |
Publisher: | WILEY-VCH Verlag GmbH & Co. KGaA |
Uncontrolled Keywords: | Perovskite phases, Oxynitrides, Solid solution, Scheelite, Magnetic properties |
Divisions: | 11 Department of Materials and Earth Sciences 11 Department of Materials and Earth Sciences > Material Science 11 Department of Materials and Earth Sciences > Material Science > Dispersive Solids |
Date Deposited: | 28 Jul 2015 07:49 |
Official URL: | http://dx.doi.org/10.1002/zaac.201500098 |
Additional Information: | Dedicated to Professor Rüdiger Kniep on the Occasion of His 70th Birthday. Special Issue: Dedicated to Professor Juri Grin on the Occasion of His 60th Birthday |
Identification Number: | doi:10.1002/zaac.201500098 |
Funders: | Funded by European Union Seventh Framework Program. Grant Number: 264873 |
Export: | |
Suche nach Titel in: | TUfind oder in Google |
![]() |
Send an inquiry |
Options (only for editors)
![]() |
Show editorial Details |