Jian, Hong ; Skokov, Konstantin P. ; Kuz'min, Michael D. ; Radulov, Iliya ; Gutfleisch, Oliver (2014)
Magnetic Properties of (Fe,Co)<sub>2</sub>B Alloys With Easy-Axis Anisotropy.
In: IEEE Transactions on Magnetics, 50 (11)
doi: 10.1109/TMAG.2014.2321458
Artikel, Bibliographie
Kurzbeschreibung (Abstract)
Intrinsic magnetic properties of (Fe 1-xCo x) 2B (x = 0.20, 0.25, 0.30, 0.35) alloys have been studied on single crystals. Temperature dependence of both magnetocrystalline anisotropy constant K 1 and spontaneous magnetization M s has been determined from magnetization isotherms measured between 10 and 1000 K. The highest anisotropy constant K 1 was obtained at x = 0.25, K 1 = 494 kJ/m 3 at T = 10 K. The Curie temperature decreased from 966 to 930 K as x increased from 0.2 to 0.35.
| Typ des Eintrags: | Artikel |
|---|---|
| Erschienen: | 2014 |
| Autor(en): | Jian, Hong ; Skokov, Konstantin P. ; Kuz'min, Michael D. ; Radulov, Iliya ; Gutfleisch, Oliver |
| Art des Eintrags: | Bibliographie |
| Titel: | Magnetic Properties of (Fe,Co)<sub>2</sub>B Alloys With Easy-Axis Anisotropy |
| Sprache: | Englisch |
| Publikationsjahr: | November 2014 |
| Verlag: | IEEE, USA |
| Titel der Zeitschrift, Zeitung oder Schriftenreihe: | IEEE Transactions on Magnetics |
| Jahrgang/Volume einer Zeitschrift: | 50 |
| (Heft-)Nummer: | 11 |
| DOI: | 10.1109/TMAG.2014.2321458 |
| Kurzbeschreibung (Abstract): | Intrinsic magnetic properties of (Fe 1-xCo x) 2B (x = 0.20, 0.25, 0.30, 0.35) alloys have been studied on single crystals. Temperature dependence of both magnetocrystalline anisotropy constant K 1 and spontaneous magnetization M s has been determined from magnetization isotherms measured between 10 and 1000 K. The highest anisotropy constant K 1 was obtained at x = 0.25, K 1 = 494 kJ/m 3 at T = 10 K. The Curie temperature decreased from 966 to 930 K as x increased from 0.2 to 0.35. |
| Fachbereich(e)/-gebiet(e): | 11 Fachbereich Material- und Geowissenschaften > Materialwissenschaft > Fachgebiet Funktionale Materialien 11 Fachbereich Material- und Geowissenschaften > Materialwissenschaft 11 Fachbereich Material- und Geowissenschaften |
| Hinterlegungsdatum: | 03 Mär 2015 12:22 |
| Letzte Änderung: | 03 Mär 2015 12:22 |
| PPN: | |
| Export: | |
| Suche nach Titel in: | TUfind oder in Google |
 |
Frage zum Eintrag |
Optionen (nur für Redakteure)
 |
Redaktionelle Details anzeigen |
Drucken
Impressum