Skourski, Y. and Bartolomé, J. and Kuz'min, M. D. and Skokov, K. P. and Bonilla, M. and Gutfleisch, O. and Wosnitza, J. (2013):
High-Field Transitions in ErFe11Ti and HoFe11Ti Single Crystals.
In: Journal of Low Temperature Physics, Springer, pp. 307-312, 170, (5-6), ISSN 0022-2291,
[Online-Edition: http://dx.doi.org/10.1007/s10909-012-0697-1],
[Article]
Official URL: http://dx.doi.org/10.1007/s10909-012-0697-1
Abstract
The magnetization of ErFe11Ti and HoFe11Ti single crystals was measured in pulsed magnetic fields up to 60 T. A number of field-induced phase transitions were observed. The inter-sublattice molecular fields were found to be 60 T in ErFe11Ti and 73 T in HoFe11Ti.
| Item Type: | Article |
|---|---|
| Erschienen: | 2013 |
| Creators: | Skourski, Y. and Bartolomé, J. and Kuz'min, M. D. and Skokov, K. P. and Bonilla, M. and Gutfleisch, O. and Wosnitza, J. |
| Title: | High-Field Transitions in ErFe11Ti and HoFe11Ti Single Crystals |
| Language: | English |
| Abstract: | The magnetization of ErFe11Ti and HoFe11Ti single crystals was measured in pulsed magnetic fields up to 60 T. A number of field-induced phase transitions were observed. The inter-sublattice molecular fields were found to be 60 T in ErFe11Ti and 73 T in HoFe11Ti. |
| Journal or Publication Title: | Journal of Low Temperature Physics |
| Volume: | 170 |
| Number: | 5-6 |
| Publisher: | Springer |
| Uncontrolled Keywords: | High field, Metamagnetic transition |
| Divisions: | 11 Department of Materials and Earth Sciences 11 Department of Materials and Earth Sciences > Material Science 11 Department of Materials and Earth Sciences > Material Science > Functional Materials |
| Date Deposited: | 26 Apr 2013 07:11 |
| Official URL: | http://dx.doi.org/10.1007/s10909-012-0697-1 |
| Identification Number: | doi:10.1007/s10909-012-0697-1 |
| Funders: | Part of this work has been supported by EuroMagNET under the EU contract No 228043. J.B. and M.B. acknowledge the MECOM project MAT11/23791 and DGA Project 34 (Fondo Social Europeo). |
| Export: |
Optionen (nur für Redakteure)
 |
View Item |
Drucken
Impressum