Crystal symmetry in single domains of PbZr0.54Ti0.46O3

Schierholz, Roland ; Fuess, Hartmut ; Tsuda, Kenji ; Ogata, Yoishiro ; Terauchi, Masami ; Theissmann, Ralf (2008)
Crystal symmetry in single domains of PbZr0.54Ti0.46O3.
In: Physical Review B, 78 (2)
doi: 10.1103/PhysRevB.78.024118
Artikel, Bibliographie

Kurzbeschreibung (Abstract)

This work focuses on the crystal symmetry of morphotropic PbZrxTi1−xO3 (PZT). The crystal symmetry is investigated within single domains of ≈30–100 nm width by convergent beam electron diffraction (CBED). The composition PbZr0.54Ti0.46O3 was chosen for experiments at room temperature and ≈300 °C. The observed zone axis symmetry at room temperature was a (1̅ 10) mirror in some domains whereas symmetry was broken in neighboring domains. Therefore the highest crystal symmetry that can be attributed with certainty to the probed volume is monoclinic. The local symmetry of single cells might be lower due to disordered displacements of the cations. At ≈300 °C the zone axis symmetry had changed to a (100)pc mirror that only occurs in the tetragonal phase of PZT.

Typ des Eintrags: Artikel
Erschienen: 2008
Autor(en): Schierholz, Roland ; Fuess, Hartmut ; Tsuda, Kenji ; Ogata, Yoishiro ; Terauchi, Masami ; Theissmann, Ralf
Art des Eintrags: Bibliographie
Titel: Crystal symmetry in single domains of PbZr0.54Ti0.46O3
Sprache: Englisch
Publikationsjahr: Juli 2008
Titel der Zeitschrift, Zeitung oder Schriftenreihe: Physical Review B
Jahrgang/Volume einer Zeitschrift: 78
(Heft-)Nummer: 2
DOI: 10.1103/PhysRevB.78.024118
Kurzbeschreibung (Abstract):

This work focuses on the crystal symmetry of morphotropic PbZrxTi1−xO3 (PZT). The crystal symmetry is investigated within single domains of ≈30–100 nm width by convergent beam electron diffraction (CBED). The composition PbZr0.54Ti0.46O3 was chosen for experiments at room temperature and ≈300 °C. The observed zone axis symmetry at room temperature was a (1̅ 10) mirror in some domains whereas symmetry was broken in neighboring domains. Therefore the highest crystal symmetry that can be attributed with certainty to the probed volume is monoclinic. The local symmetry of single cells might be lower due to disordered displacements of the cations. At ≈300 °C the zone axis symmetry had changed to a (100)pc mirror that only occurs in the tetragonal phase of PZT.

Zusätzliche Informationen:

SFB 595 B3

Fachbereich(e)/-gebiet(e): DFG-Sonderforschungsbereiche (inkl. Transregio) > Sonderforschungsbereiche > SFB 595: Elektrische Ermüdung > B - Charakterisierung > Teilprojekt B3: Strukturelle Untersuchungen zur Aufklärung der elektrischen Ermüdung in PZT
DFG-Sonderforschungsbereiche (inkl. Transregio) > Sonderforschungsbereiche > SFB 595: Elektrische Ermüdung > B - Charakterisierung
DFG-Sonderforschungsbereiche (inkl. Transregio) > Sonderforschungsbereiche > SFB 595: Elektrische Ermüdung
Zentrale Einrichtungen
DFG-Sonderforschungsbereiche (inkl. Transregio) > Sonderforschungsbereiche
DFG-Sonderforschungsbereiche (inkl. Transregio)
Hinterlegungsdatum: 10 Aug 2011 11:38
Letzte Änderung: 05 Mär 2013 09:51
PPN:
Export:
Suche nach Titel in: TUfind oder in Google
Frage zum Eintrag Frage zum Eintrag

Optionen (nur für Redakteure)
Redaktionelle Details anzeigen Redaktionelle Details anzeigen