Effect factors on thermal and mechanical properties of SiO2 and TiB2 modified SiBCN-based adhesives

Luan, Xin’gang ; Li, Min ; Chang, Sen ; Li, Yongguo ; Wang, Kunjun ; Song, Xuemei ; Riedel, Ralf ; Cheng, Laifei (2020)
Effect factors on thermal and mechanical properties of SiO2 and TiB2 modified SiBCN-based adhesives.
In: Ceramics International / Part B, 46 (11)
doi: 10.1016/j.ceramint.2020.04.286
Artikel, Bibliographie

Kurzbeschreibung (Abstract)

To further investigate the reinforcing factors on the adhesion strength of SiO2 and TiB2 modified SiBCN-based adhesives, the thermal stability analysis, microstructure observations and phase composition analysis were performed on four kinds of modified PSNB (Polyborosilazane) adhesives. With the different Si/B ratio and SiO2 content, the room temperature adhesion strength reach up to 18.95, 12.04, 32.44 and 13.69 MPa for PPT-1, PPT-2, PPTS and PST respectively, after synthesized at 1000 degrees C in air. And then, the high temperature adhesion strength reach up to 12.3 and 16.4 MPa for PPT-1 and PPTS at 1000 degrees C in vacuum, respectively. Interestingly, it has been found that temperature, PSO, solid content and SiO2 content all have a great influence on the adhesion performance of SiO2 and TiB2 modified SiBCN-based adhesives.

Typ des Eintrags: Artikel
Erschienen: 2020
Autor(en): Luan, Xin’gang ; Li, Min ; Chang, Sen ; Li, Yongguo ; Wang, Kunjun ; Song, Xuemei ; Riedel, Ralf ; Cheng, Laifei
Art des Eintrags: Bibliographie
Titel: Effect factors on thermal and mechanical properties of SiO2 and TiB2 modified SiBCN-based adhesives
Sprache: Englisch
Publikationsjahr: 1 August 2020
Verlag: Elsevier
Titel der Zeitschrift, Zeitung oder Schriftenreihe: Ceramics International / Part B
Jahrgang/Volume einer Zeitschrift: 46
(Heft-)Nummer: 11
DOI: 10.1016/j.ceramint.2020.04.286
URL / URN: https://www.sciencedirect.com/science/article/pii/S027288422...
Kurzbeschreibung (Abstract):

To further investigate the reinforcing factors on the adhesion strength of SiO2 and TiB2 modified SiBCN-based adhesives, the thermal stability analysis, microstructure observations and phase composition analysis were performed on four kinds of modified PSNB (Polyborosilazane) adhesives. With the different Si/B ratio and SiO2 content, the room temperature adhesion strength reach up to 18.95, 12.04, 32.44 and 13.69 MPa for PPT-1, PPT-2, PPTS and PST respectively, after synthesized at 1000 degrees C in air. And then, the high temperature adhesion strength reach up to 12.3 and 16.4 MPa for PPT-1 and PPTS at 1000 degrees C in vacuum, respectively. Interestingly, it has been found that temperature, PSO, solid content and SiO2 content all have a great influence on the adhesion performance of SiO2 and TiB2 modified SiBCN-based adhesives.

Freie Schlagworte: Si/B ratio; SiO2 content; SiBCN-based ceramic; Adhesion strength CERAMICS; STRENGTH; JOINT
Fachbereich(e)/-gebiet(e): 11 Fachbereich Material- und Geowissenschaften
11 Fachbereich Material- und Geowissenschaften > Materialwissenschaft
11 Fachbereich Material- und Geowissenschaften > Materialwissenschaft > Fachgebiet Disperse Feststoffe
Hinterlegungsdatum: 23 Jun 2020 06:22
Letzte Änderung: 23 Jun 2020 06:22
PPN:
Projekte: Research Fund of the National Key Research and Development Program of China, Grant Number 2017YFB0703200, National Natural Science Foundation of China, Grant Number 91960105, National Basic Research Program of China, State Key Laboratory on Integrated Optoelectronics, China, Grant Number IOSKL2018KF05
Export:
Suche nach Titel in: TUfind oder in Google
Frage zum Eintrag Frage zum Eintrag

Optionen (nur für Redakteure)
Redaktionelle Details anzeigen Redaktionelle Details anzeigen